- additive manufacturing; polylactic acid (PLA); fused filament fabrication (FFF); fused deposition modeling (FDM); printing temperature; filament color; dimensional accuracy; tensile strength; friction performance; wear (1)
- corrosion; self-fluxing alloys; NiCrBSi; WC-12Co; cavitation; hard metals (1)
Flame-sprayed NiCrBSi/WC-12Co composite coatings were deposited in different ratios on the surface of stainless steel. Oxyacetylene flame remelting treatment was applied to surfaces for refinement of the morphology of the layers and improvement of the coating/substrate adhesion.
The performance of the coated specimens to cavitation erosion and electrochemical corrosion was evaluated by an ultrasonic vibratory method and, respectively, by polarization measurements. The microstructure was investigated by means of scanning electron microscopy (SEM) combined with energy dispersive X-ray analysis (EDX). The obtained results demonstrated that the addition of 15 wt.% WC-12Co to the self-fluxing alloy improves the resistance to cavitation erosion (the terminal erosion rate (Vs) decreased with 15% related to that of the NiCrBSi coating) without influencing the good corrosion resistance in NaCl solution. However, a further increase in WC-Co content led to a deterioration of these coating properties (the Vs has doubled related to that of the NiCrBSi coating).
Moreover, the corrosion behavior of the latter composite coating was negatively influenced, a fact confirmed by increased values for the corrosion current density (icorr). Based on the achieved experimental results, one may summarize that NiCrBSi/WC-Co composite coatings are able to increase the life cycle of expensive, high-performance components exposed to severe cavitation conditions.
The printing variable least addressed in previous research aiming to reveal the effect of the FFF process parameters on the printed PLA part’s quality and properties is the filament color. Moreover, the color of the PLA, as well as its manufacturer, are rarely mentioned when the experimental conditions for the printing of the samples are described, although current existing data reveal that their influence on the final characteristics of the print should not be neglected. In order to point out the importance of this influential parameter, a natural and a black-colored PLA filament, produced by the same manufacturer, were selected. The dimensional accuracy, tensile strength, and friction properties of the samples were analyzed and compared for printing temperatures ranging from 200 C up to 240 C. The experimental results clearly showed different characteristics depending on the polymer color of samples printed under the same conditions. Therefore, the optimization of the FFF process parameters for the 3D-printing of PLA should always start with the proper selection of the type of the PLA material, regarding both its color and the fabricant.