Based on the fact that titanium and titanium alloys have poor fretting fatigue resistance and poor tribological properties, it is necessary to apply some surface engineering methods in order to increase the exploitation characteristics of these materials. One may either implement some surface treatment technologies or even deposit overlay coatings by thermal spraying.
The present study is focused on the achieved properties of the ceramic coatings (Al2O3 + 13 wt.% TiO2) deposited onto a titanium substrate using high velocity oxygen fuel (HVOF) and plasma spraying (APS) respectively.
The effect of the deposition method on the microstructure, phase constituents, and mechanical properties of the ceramic coatings was investigated by means of scanning electron microscopy (SEM), X-ray diffraction technique (XRD) and nanoindentation tests. The sliding wear performances of the Al2O3–TiO2 coatings were tested using a pin on disk wear tester.
Tape brazing constitutes a cost-effective alternative surface protection technology for complex-shaped surfaces. The study explores the characteristics of high-temperature brazed coatings using a cobalt-based powder deposited on a stainless-steel substrate in order to protect parts subjected to hot temperatures in a wear-exposed environment. Microstructural imaging corroborated with x-ray diffraction analysis showed a complex phased structure consisting of intermetallic Cr-Ni, C-Co-W Laves type, and chromium carbide phases. The surface properties of the coatings, targeting hot corrosion behavior, erosion, wear resistance, and microhardness, were evaluated. The high-temperature corrosion test was performed for 100 h at 750 C in a salt mixture consisting of 25 wt.% NaCl + 75 wt.% Na2SO4. The degree of corrosion attack was closely connected with the exposure temperature, and the degradation of the material corresponding to the mechanisms of low-temperature hot corrosion. The erosion tests were carried out using alumina particles at a 90 impingement angle. The results, correlated with the microhardness measurements, have shown that Co-based coatings exhibited approximately 40% lower material loss compared to that of the steel substrate.