- water electrolysis (2)
- PEMWE (1)
- bipolar plate (1)
- coatings (1)
- corrosion resistance (1)
- hydraulic cell compression (1)
- novel (1)
- polymer electrolyte membrane (1)
For proton exchange membrane water electrolysis (PEMWE) to become competitive, the cost of stack components, such as bipolar plates (BPP), needs to be reduced. This can be achieved by using coated low-cost materials, such as copper as alternative to titanium. Herein we report on highly corrosion-resistant copper BPP coated with niobium. All investigated samples showed excellent corrosion resistance properties, with corrosion currents lower than 0.1 µA cm−2 in a simulated PEM electrolyzer environment at two different pH values. The physico-chemical properties of the Nb coatings are thoroughly characterized by scanning electron microscopy (SEM), electrochemical impedance spectroscopy (EIS), X-ray photoelectron spectroscopy (XPS), and atomic force microscopy (AFM). A 30 µm thick Nb coating fully protects the Cu against corrosion due to the formation of a passive oxide layer on its surface, predominantly composed of Nb2O5. The thickness of the passive oxide layer determined by both EIS and XPS is in the range of 10 nm. The results reported here demonstrate the effectiveness of Nb for protecting Cu against corrosion, opening the possibility to use it for the manufacturing of BPP for PEMWE. The latter was confirmed by its successful implementation in a single cell PEMWE based on hydraulic compression technology.
In this work, a novel polymer electrolyte membrane water electrolyzer (PEMWE) test cell based on hydraulic single-cell compression is described. In this test cell, the current density distribution is almost homogeneous over the active cell area due to hydraulic cell clamping. As the hydraulic medium entirely surrounds the active cell components, it is also used to control cell temperature resulting in even temperature distribution. The PEMWE single-cell test system based on hydraulic compression offers a 25 cm2 active surface area (5.0 × 5.0 cm) and can be operated up to 80°C and 6.0 A/cm2. Construction details and material selection for the designed test cell are given in this document. Furthermore, findings related to pressure distribution analyzed by utilizing a pressure-sensitive foil, the cell performance indicated by polarization curves, and the reproducibility of results are described. Experimental data indicate the applicability of the presented testing device for relevant PEMWE component testing and material analysis.