Westfälisches Energieinstitut
Refine
Year of publication
Document Type
- Conference Proceeding (13)
- Article (7)
Has Fulltext
- no (20) (remove)
Keywords
- carbon nanofibers, platinum electrodeposition, ele ctrochemical surface area (1)
- AEM-Electrolysis (1)
- Electrodeposition (1)
- Hydraulic compression, Carbon Nano Fibers, PEM Fuel Cells, Catalyst utilization (1)
- Hydrogen evolution reaction (1)
- Ni-Mo alloy Catalyst (1)
- PEM fuel cell electrocatalysts, Carbon nanofibers, Oxygen plasma activation, Pulsed electroplating. (1)
- PEM water electrolysis (1)
- PtCoMn (1)
- Ternary alloy catalyst preparation (1)
A systematic method for obtaining a novel electrode structure based on PtCoMn ternary alloy catalyst supported on graphitic carbon nanofibers (CNF) for hydrogen evolution reaction (HER) in acidic media is proposed. Ternary alloy nanoparticles (Co0.6Mn0.4 Pt), with a mean crystallite diameter under 10 nm, were electrodeposited onto a graphitic support material using a two-step pulsed deposition technique. Initially, a surface functionalisation of the carbon nanofibers is performed with the aid of oxygen plasma. Subsequently, a short galvanostatic pulse electrodeposition technique is applied. It has been demonstrated that, if pulsing current is employed, compositionally controlled PtCoMn catalysts can be achieved. Variations of metal concentration ratios in the electrolyte and main deposition parameters, such as current density and pulse shape, led to electrodes with relevant catalytic activity towards HER. The samples were further characterised using several physico-chemical methods to reveal their morphology, structure, chemical and electrochemical properties. X-ray diffraction confirms the PtCoMn alloy formation on the graphitic support and energy dispersive X-ray spectroscopy highlights the presence of the three metallic components from the alloy structure. The preliminary tests regarding the electrocatalytic activity of the developed electrodes display promising results compared to commercial Pt/C catalysts. The PtCoMn/CNF electrode exhibits a decrease in hydrogen evolution overpotential of about 250 mV at 40 mA cm−2 in acidic solution (0.5 M H2SO4) when compared to similar platinum based electrodes (Pt/CNF) and a Tafel slope of around 120 mV dec−1, indicating that HER takes place under the Volmer-Heyrovsky mechanism.
To further increase platinum utilisation in PEM fuel cells CNFs are investigated as catalyst support material due to the CNF’s high specific surface area. Furthermore, CNFs provide suitable properties concerning corrosion resistance as well as electrical conductivity in contrast to conventional carbon supports.
This work presents the results of an electrode preparation procedure based on O2 plasma activated CNFs. The plasma treatment leads to CNF dispersibility in alcohol/water for a spray coating process. Furthermore, O2 plasma activation enhances metal deposition on the CNF’s surface. Pulse plating procedure as well as wet chemical metal synthesis have been used for particle deposition. For pulse plating a potentiostat/galvanostat type MMates 510 AC from Materials Mates, Italy has been used. Electrode morphology has been determined in SEM type XL 30 ESEM from Philips, The Netherlands.
Platinum nanoparticles electrodeposition on carbon nanofibers (CNF) support has been performed with the purpose to obtain electrodes that can be further used especially in a polymer electrolyte membrane fuel cell (PEMFC). A pretreatment of CNF is required in order to enhance the surface energy, which simultaneously improves handling and wettability as well as interaction with the platinum cations. This step was performed using oxygen plasma functionalization. To produce CNF supported Pt catalysts, an electrochemical method was applied and the deposition parameters were adjusted to obtain nanosized platinum particles with a good distribution onto the graphitic surface. The morphology and structure of the obtained particles were investigated by scanning electron microscopy combined with energy dispersive X-Ray spectroscopy. The amount of deposited platinum was established using thermogravimetrical measurements. Cyclic voltammetry performed in 0.5 M H2SO4 solution was applied for determining the electrochemical surface area (ECSA) of the obtained electrodes.The functionalization degree of the CNF outer surface has a strong influence on the structure, distribution and amount of platinum particles. Moreover, the current densities, which were set for the deposition process influenced not only the particles size but also the platinum amount. Applying an oxygen plasma treatment of 80 W for 1800 s, the necessary degree of surface functionalization is achieved in order to deposit the catalyst particles. The best electrodes were prepared using a current density of 50 mA cm-2 during the deposition process that leads to a homogenous platinum distribution with particles size under 80 nm and ECSA over 6 cm2
In polymer electrolyte membrane fuel cells (PEMFC) noble metal nano particles are deposited on graphitic supports serving as electrocatalysts for devices with high power density. In this study anodes are analysed with low platinum loading of about 0.1 mg cm-2. These electrodes are prepared by carbon nano fibres (CNF) decorated with platinum nano particles. For electrode manufacturing two sorts of fibres, which are produced in an industrial scale, are used with different graphitisation degree and surface area. CNF layers are applied on commercially available graphitic substrate by spray coating which leads to a porous structure with high surface area. Subsequently, platinum deposition is achieved by pulsed electroplating for an improved platinum utilisation in PEMFC electrodes. Spray coating and platinum deposition are assisted by a previous oxygen plasma activation process. Prepared anode material is characterised by scanning electron microscopy (SEM), transmission electron microscopy (TEM), X-ray diffraction spectroscopy (XRD), X-ray fluorescence spectroscopy (XRF) and thermogravimetry (TGA). Electrochemical analyses (cyclic voltammetry and corrosion test) are carried out in 0.5 M sulphuric acid. The effect of graphitisation degree of carbon nano fibres on the performance of prepared electrodes is investigated in-situ in a PEM fuel cell test bench.