The diffusion of hydrogen adsorbed inside layered MoS2 crystals has been studied by means of quasi- elastic neutron scattering, neutron spin-echo spectroscopy, nuclear reaction analysis, and X-ray photoelectron spectroscopy. The neutron time-of-flight and neutron spin-echo measurements demonstrate fast diffusion of hydrogen molecules parallel to the basal planes of the two dimensional crystal planes. At room temperature and above, this intra-layer diffusion is of a similar speed to the surface diffusion that has been observed in earlier studies for hydrogen atoms on Pt surfaces. A significantly slower hydrogen diffusion was observed perpendicular to the basal planes using nuclear reaction analysis.
The one-phonon inelastic low energy helium atom scattering theory is adapted to cases where the target monolayer is a p(1x1) commensurate square lattice. Experimental data for para-H2/NaCl(001) are re-analyzed and the relative intensities of energy loss peaks in the range 6 to 9 meV are determined. The case of the H2/NaCl(001) monolayer for 26 meV scattering energy is computationally challenging and difficult because it has a much more corrugated surface than those in the previous applications for triangular lattices. This requires a large number of coupled channels for convergence in the wave-packet-scattering calculation and a long series of Fourier amplitudes to represent the helium-target potential energy surface. A modified series is constructed in which a truncated Fourier expansion of the potential is constrained to give the exact value of the potential at some key points and which mimics the potential with fewer Fourier amplitudes. The shear horizontal phonon mode is again accessed by the helium scattering for small misalignment of the scattering plane relative to symmetry axes of the monolayer. For 1° misalignment, the calculated intensity of the longitudinal acoustic phonon mode frequently is higher than that of the shear horizontal phonon mode in contrast to what was found at scattering energies near 10 meV for triangular lattices of Ar, Kr, and Xe on Pt(111).
Hydrogen concentrations in ZnO single crystals exposing different surfaces have been determined to be in the range of (0.02–0.04) at.% with an error of ±0.01 at.% using nuclear reaction analysis. In the subsurface region, the hydrogen concentration has been determined to be higher by up to a factor of 10. In contrast to the hydrogen in the bulk, part of the subsurface hydrogen is less strongly bound, can be removed by heating to 550°C, and reaccommodated by loading with atomic hydrogen. By exposing the ZnO(10-10) surface to water above room temperature and to atomic hydrogen, respectively, hydroxylation with the same coverage of hydrogen is observed.