Filtern
Dokumenttyp
Volltext vorhanden
- nein (16) (entfernen)
Schlagworte
- carbon nanofibers, platinum electrodeposition, ele ctrochemical surface area (1)
- Hydraulic compression, Carbon Nano Fibers, PEM Fuel Cells, Catalyst utilization (1)
- Hydrogen evolution reaction (1)
- PEM fuel cell electrocatalysts, Carbon nanofibers, Oxygen plasma activation, Pulsed electroplating. (1)
- PEM water electrolysis (1)
- PtCoMn (1)
- Ternary alloy catalyst preparation (1)
- carbon nanofibers, platinum electrodeposition, electrocatalysts (1)
Institut
- Westfälisches Energieinstitut (16) (entfernen)
Platinum nanoparticles electrodeposition on carbon nanofibers (CNF) support has been performed with the purpose to obtain electrodes that can be further used especially in a polymer electrolyte membrane fuel cell (PEMFC). A pretreatment of CNF is required in order to enhance the surface energy, which simultaneously improves handling and wettability as well as interaction with the platinum cations. This step was performed using oxygen plasma functionalization. To produce CNF supported Pt catalysts, an electrochemical method was applied and the deposition parameters were adjusted to obtain nanosized platinum particles with a good distribution onto the graphitic surface. The morphology and structure of the obtained particles were investigated by scanning electron microscopy combined with energy dispersive X-Ray spectroscopy. The amount of deposited platinum was established using thermogravimetrical measurements. Cyclic voltammetry performed in 0.5 M H2SO4 solution was applied for determining the electrochemical surface area (ECSA) of the obtained electrodes.The functionalization degree of the CNF outer surface has a strong influence on the structure, distribution and amount of platinum particles. Moreover, the current densities, which were set for the deposition process influenced not only the particles size but also the platinum amount. Applying an oxygen plasma treatment of 80 W for 1800 s, the necessary degree of surface functionalization is achieved in order to deposit the catalyst particles. The best electrodes were prepared using a current density of 50 mA cm-2 during the deposition process that leads to a homogenous platinum distribution with particles size under 80 nm and ECSA over 6 cm2
This experimental work deals with the preparation and investigation of PEM fuel cell electrodes, which are obtained using Graphene Related Material (GRM) serving as catalyst support material for platinum nanoparticles. The applied GRM belong to the group of carbon nanofibers and exhibits a helical-ribbon structure with dimensions of 50 nm in diameter and an average length up to a few µm. Furthermore, utilized GRM provide a superior graphitisation degree of about 100 %, which leads to both high corrosion resistance and low ohmic resistance. Material stability plays one of the main roles for long term fuel cell operation, whereby a great electrical catalyst contact combined with high specific surface area yields in high fuel cell performances.
Prior to GRM dispersion and deposition onto a gas diffusion layer, the graphene structures are functionalized by oxygen plasma treatment. Through this step, functional oxygen groups are generated onto the GRM outer surface providing an improved hydrophilic behaviour and facilitating the GRM suspension preparation. In addition, the oxygen groups act as anchors for platinum nanoparticles which are subsequently deposited onto the GRM surface through a pulse electrodeposition process.
Membrane electrode assemblies produced with the prepared electrodes are investigated in-situ in a PEM fuel cell test bench.
A systematic method for obtaining a novel electrode structure based on PtCoMn ternary alloy catalyst supported on graphitic carbon nanofibers (CNF) for hydrogen evolution reaction (HER) in acidic media is proposed. Ternary alloy nanoparticles (Co0.6Mn0.4 Pt), with a mean crystallite diameter under 10 nm, were electrodeposited onto a graphitic support material using a two-step pulsed deposition technique. Initially, a surface functionalisation of the carbon nanofibers is performed with the aid of oxygen plasma. Subsequently, a short galvanostatic pulse electrodeposition technique is applied. It has been demonstrated that, if pulsing current is employed, compositionally controlled PtCoMn catalysts can be achieved. Variations of metal concentration ratios in the electrolyte and main deposition parameters, such as current density and pulse shape, led to electrodes with relevant catalytic activity towards HER. The samples were further characterised using several physico-chemical methods to reveal their morphology, structure, chemical and electrochemical properties. X-ray diffraction confirms the PtCoMn alloy formation on the graphitic support and energy dispersive X-ray spectroscopy highlights the presence of the three metallic components from the alloy structure. The preliminary tests regarding the electrocatalytic activity of the developed electrodes display promising results compared to commercial Pt/C catalysts. The PtCoMn/CNF electrode exhibits a decrease in hydrogen evolution overpotential of about 250 mV at 40 mA cm−2 in acidic solution (0.5 M H2SO4) when compared to similar platinum based electrodes (Pt/CNF) and a Tafel slope of around 120 mV dec−1, indicating that HER takes place under the Volmer-Heyrovsky mechanism.