Filtern
Dokumenttyp
- Konferenzveröffentlichung (13) (entfernen)
Volltext vorhanden
- nein (13) (entfernen)
In state of the art polymer electrolyte membrane fuel cells (PEMFC) rare and expensive platinum group metals (PGM) are used as catalyst material. Reduction of PGM in PEMFC electrodes is strongly required to reach cost targets for this technology. An optimal catalyst utilisation is achieved in the case of nano-structured particles supported on carbon material with a large specific surface area. In this study, graphitic material in form of carbon nanofibres (CNFs) is decorated with platinum (Pt) particles serving as catalyst material for PEMFC electrodes with low Pt loading. For electrode preparation CNFs have been previously activated by means of radio frequency induced oxygen plasma. This kind of treatment results in formation of functional groups on the CNF’s surface which directly influences the characteristics of subsequent Pt particle deposition. Different plasma parameters (plasma power, gas flow or exposure time) have to be set in order to achieve formation of oxygen containing functional groups (hydroxylic, carboxylic or carbonylic) on the CNF’s surface. In the frame of this experimental work, electrodes are investigated in respect of optimal morphology, microstructure as well as electrochemical properties. Therefore, samples were characterised by means of scanning electron microscopy combined with energy dispersive X-ray analysis, transmission electron microscopy, thermogravimetry, X-ray diffraction, X-ray fluorescence as well as polarisation measurements.
To further increase platinum utilisation in PEM fuel cells CNFs are investigated as catalyst support material due to the CNF’s high specific surface area. Furthermore, CNFs provide suitable properties concerning corrosion resistance as well as electrical conductivity in contrast to conventional carbon supports.
This work presents the results of an electrode preparation procedure based on O2 plasma activated CNFs. The plasma treatment leads to CNF dispersibility in alcohol/water for a spray coating process. Furthermore, O2 plasma activation enhances metal deposition on the CNF’s surface. Pulse plating procedure as well as wet chemical metal synthesis have been used for particle deposition. For pulse plating a potentiostat/galvanostat type MMates 510 AC from Materials Mates, Italy has been used. Electrode morphology has been determined in SEM type XL 30 ESEM from Philips, The Netherlands.
The membrane electrode assemblies (MEA) for polymer electrolyte membrane fuel cells (PEMFC) developed at the Westphalian Energy Institute are based on oxygen plasma activated carbon nanotubes (CNT) doped with platinum particles. For electrode preparation an ink is used containing the activated CNTs as well as hydrophobic and hydrophilic material in solved form. After this ink is sprayed onto a graphitic substrate platinum particles are deposited by pulse plating method, where the plasma activation enhances CNT dispersibility as well as platinum deposition. This materials mixture is structured in nanoscale with the aim to increase the catalyst particles’ specific surface. For low reactance at operation, homogeneous compression of the MEA’s layers is necessary within a PEMFC. A novel stack architecture for electrochemical cells, especially PEMFC as well as PEM electrolysers, has been developed in order to achieve ideal cell operation conditions. Single cells of such a stack are inserted into flexible slots that are surrounded by a hydraulic medium which is pressurised during operation in order to achieve an even compression and cooling of the stack’s cells. With this stack design it has been possible to construct a test facility for simultaneous characterisation of several MEA samples. As compression and temperature conditions of every single sample are the same, the effects of e.g. different electrode configurations can be investigated with the novel test system.