For proton exchange membrane water electrolysis (PEMWE) to become competitive, the cost of stack components, such as bipolar plates (BPP), needs to be reduced. This can be achieved by using coated low-cost materials, such as copper as alternative to titanium. Herein we report on highly corrosion-resistant copper BPP coated with niobium. All investigated samples showed excellent corrosion resistance properties, with corrosion currents lower than 0.1 µA cm−2 in a simulated PEM electrolyzer environment at two different pH values. The physico-chemical properties of the Nb coatings are thoroughly characterized by scanning electron microscopy (SEM), electrochemical impedance spectroscopy (EIS), X-ray photoelectron spectroscopy (XPS), and atomic force microscopy (AFM). A 30 µm thick Nb coating fully protects the Cu against corrosion due to the formation of a passive oxide layer on its surface, predominantly composed of Nb2O5. The thickness of the passive oxide layer determined by both EIS and XPS is in the range of 10 nm. The results reported here demonstrate the effectiveness of Nb for protecting Cu against corrosion, opening the possibility to use it for the manufacturing of BPP for PEMWE. The latter was confirmed by its successful implementation in a single cell PEMWE based on hydraulic compression technology.
This report gives a brief overview to the state of the art of PEM fuel cell technology and a description of a newly developed fuel cell stack concept. One main research activity at the Westphalian Energy Institute of the Westphalian University of Applied Sciences is the development of PEM fuel cells, for which a range of different materials have been investigated for fuel cell pole plate construction. Whereas graphite is a material which has suitable properties concerning conductivity as well as manufacturing e.g. for milling, stainless steel foils are suitable for economical hydroforming processes. However, with steel coating is necessary to increase corrosion resistance as well as electrical conductivity. A new fuel cell stack design is currently under development using separated single fuel cells with hydraulic cell compression. The advantages of this stack concept are modularity, effective heat exchanging and constant, uniform cell compression which are further described in this work.
In this study, a novel design concept for PEMFC (polymer electrolytemembrane fuel cell) stacks is presented with singlecells inserted in pockets surrounded by a hydraulic medium. Thehydraulic pressure introduces necessary compression forces to themembrane electrode assembly of each cell within a stack. Moreover, homogeneous cell cooling is achieved by this medium. First,prototypes presented in this work indicate that, upscaling of cells for the novelstack design is possible without significantperformancelosses. Due to its modularity and scalability, this stackdesign meets the requirements for large PEMFC units.
Hydrogen produced via water electrolysis powered by renewable electricity or green H2 offers new decarbonization pathways. Proton exchange membrane water electrolysis (PEMWE) is a promising technology although the current density, temperature, and H2 pressure of the PEMWE will have to be increased substantially to curtail the cost of green H2. Here, a porous transport layer for PEMWE is reported, that enables operation at up to 6 A cm−2, 90 °C, and 90 bar H2 output pressure. It consists of a Ti porous sintered layer (PSL) on a low‐cost Ti mesh (PSL/mesh‐PTL) by diffusion bonding. This novel approach does not require a flow field in the bipolar plate. When using the mesh‐PTL without PSL, the cell potential increases significantly due to mass transport losses reaching ca. 2.5 V at 2 A cm−2 and 90 °C.
The technology of polymer electrolyte membrane (PEM) electrolysis provides an efficient way to produce hydrogen. In combination with renewable energy sources, it promises to be one of the key factors towards a carbon-free energy infrastructure in the future. Today, PEM electrolyzers with a power consumption higher than 1 MW and a gas output pressure of 30 bar (or even higher) are already commercially available. Nevertheless, fundamental research and development for an improved efficiency is far from being finally accomplished, and mostly takes place on a laboratory scale. Upscaling the laboratory prototypes to an industrial size usually cannot be achieved without facing further problems and/or losing efficiency. With our novel system design based on hydraulic cell compression, a lot of the commonly occurring problems like inhomogeneous temperature and current distribution can be avoided. In this study we present first results of an upscaling by a factor of 30 in active cell area.
In this work, a novel polymer electrolyte membrane water electrolyzer (PEMWE) test cell based on hydraulic single-cell compression is described. In this test cell, the current density distribution is almost homogeneous over the active cell area due to hydraulic cell clamping. As the hydraulic medium entirely surrounds the active cell components, it is also used to control cell temperature resulting in even temperature distribution. The PEMWE single-cell test system based on hydraulic compression offers a 25 cm2 active surface area (5.0 × 5.0 cm) and can be operated up to 80°C and 6.0 A/cm2. Construction details and material selection for the designed test cell are given in this document. Furthermore, findings related to pressure distribution analyzed by utilizing a pressure-sensitive foil, the cell performance indicated by polarization curves, and the reproducibility of results are described. Experimental data indicate the applicability of the presented testing device for relevant PEMWE component testing and material analysis.