- carbon nanofibers, platinum electrodeposition, ele ctrochemical surface area (1)
- AEM-Electrolysis (1)
- Electrodeposition (1)
- Erneuerbare Energien (1)
- Hydraulic compression, Carbon Nano Fibers, PEM Fuel Cells, Catalyst utilization (1)
- Hydrogen evolution reaction (1)
- Kohlenstoff-Nanoröhre (1)
- Ni-Mo alloy Catalyst (1)
- PEM fuel cell electrocatalysts, Carbon nanofibers, Oxygen plasma activation, Pulsed electroplating. (1)
- PEM water electrolysis (1)
- Polymer-Elektrolytmembran-Brennstoffzelle (1)
- PtCoMn (1)
- Ternary alloy catalyst preparation (1)
- carbon nanofibers, platinum electrodeposition, electrocatalysts (1)
Various aqueous citrate electrolyte compositions for the Ni-Mo electrodeposition are explored in order to deposit Ni-Mo alloys with Mo-content ranging from 40 wt% to 65 wt% to find an alloy composition with superior catalytic activity towards the hydrogen evolution reaction (HER). The depositions were performed on copper substrates mounted onto a rotating disc electrode (RDE) and were investigated via scanning electron microscopy (SEM), X-ray fluorescence (XRF) and X-ray diffraction (XRD) methods as well as linear sweep voltammetry (LSV) and impedance spectroscopy. Kinetic parameters were calculated via Tafel analysis. Partial deposition current densities and current efficiencies were determined by correlating XRF measurements with gravimetric results. The variation of the electrolyte composition and deposition parameters enabled the deposition of alloys with Mo-content over the range of 40-65 wt%. An increase in Mo-content in deposited alloys was recorded with an increase in rotation speed of the RDE. Current efficiency of the deposition was in the magnitude of <1%, which is characteristic for the deposition of alloys with high Mo-content. The calculated kinetic parameters were used to determine the Mo-content with the highest catalytic activity for use in the HER.
A systematic method for obtaining a novel electrode structure based on PtCoMn ternary alloy catalyst supported on graphitic carbon nanofibers (CNF) for hydrogen evolution reaction (HER) in acidic media is proposed. Ternary alloy nanoparticles (Co0.6Mn0.4 Pt), with a mean crystallite diameter under 10 nm, were electrodeposited onto a graphitic support material using a two-step pulsed deposition technique. Initially, a surface functionalisation of the carbon nanofibers is performed with the aid of oxygen plasma. Subsequently, a short galvanostatic pulse electrodeposition technique is applied. It has been demonstrated that, if pulsing current is employed, compositionally controlled PtCoMn catalysts can be achieved. Variations of metal concentration ratios in the electrolyte and main deposition parameters, such as current density and pulse shape, led to electrodes with relevant catalytic activity towards HER. The samples were further characterised using several physico-chemical methods to reveal their morphology, structure, chemical and electrochemical properties. X-ray diffraction confirms the PtCoMn alloy formation on the graphitic support and energy dispersive X-ray spectroscopy highlights the presence of the three metallic components from the alloy structure. The preliminary tests regarding the electrocatalytic activity of the developed electrodes display promising results compared to commercial Pt/C catalysts. The PtCoMn/CNF electrode exhibits a decrease in hydrogen evolution overpotential of about 250 mV at 40 mA cm−2 in acidic solution (0.5 M H2SO4) when compared to similar platinum based electrodes (Pt/CNF) and a Tafel slope of around 120 mV dec−1, indicating that HER takes place under the Volmer-Heyrovsky mechanism.
Carbon Nanofibers (CNF) are considered to be a promising catalyst support material due to their unique characteristics, excellent mechanical, electrical and structural properties, high surface area and nevertheless, good interaction with metallic catalyst particles. The possibility of preparing CNF decorated with platinum by an electrochemical method was tested, using a hexachloroplatinic bath solution. The experiments were carried out with the aid of a Potentiostat/Galvanostat Ivium Technologies Vertex, in a three – electrode cell. The aim of the present work was to determine the electrochemical surface area (ECSA) of the CNF-Pt catalysts in relation to the functionalization treatment of fibers, using an electrochemical method. ECSA for different functionalized CNF-Pt catalysts was determined by cyclic voltammetry in 0.5 M H2SO4 solution. The highest active surface of platinum was obtained for the samples with CNF functionalized by plasma treatment using 80 W for 1800 s. The obtained results correlate very well with the particles size and distribution of platinum, revealed by scanning electron microscopy (SEM) and the quantity of deposited platinum determined by thermo gravimetrical analysis (TGA) respectively. Cyclic voltammetry (CV) has been proven to be a suitable method for estimation of the ECSA of the electrocatalysts.
This work deals with the preparation and investigation of PEM fuel cell electrodes, which are obtained using graphene related material (GRM) serving as catalyst support for platinum nanoparticles. Applied GRM are used for the preparation of suspensions in four distinct mixing ratios. Two sorts of GRM have been investigated: carbon nanofibers (CNF) and graphene oxide (GO). Utilized CNFs provide a superior graphitization degree of about 100%, which leads to both high corrosion resistance and low ohmic resistance in PEM fuel cells.
For electrode preparation a GRM containing layer serving as catalyst support is applied onto a gas diffusion layer (GDL). Prior to GRM suspension and deposition onto a GDL, the graphene structures are functionalized by plasma treatment. Due to this step, an improved hydrophilic behavior for facilitating suspension preparation is achieved. In addition, a subsequent platinum nanoparticle deposition by pulsed electrodeposition process is optimized.