Schlagworte
- carbon nanofibers, platinum electrodeposition, ele ctrochemical surface area (1)
- AEM-Electrolysis (1)
- Additive manufacturing Directed energy deposition-arc 316L stainless steel Corrosion behavior Electrochemical corrosion (1)
- Cavitation; Corrosion; Laser remelting; Self-fluxing alloys; Stellite 6 (1)
- Electrodeposition (1)
- Hydraulic compression, Carbon Nano Fibers, PEM Fuel Cells, Catalyst utilization (1)
- Hydrogen evolution reaction (1)
- Ni-Mo alloy Catalyst (1)
- NiCrBSi coatings; flame spraying; induction remelting; wear resistance (1)
- PEM fuel cell electrocatalysts, Carbon nanofibers, Oxygen plasma activation, Pulsed electroplating. (1)
Institut
Without proper post-processing (often using flame, furnace, laser remelting, and induction) or reinforcements’ addition, Ni-based flame-sprayed coatings generally manifest moderate adhesion to the substrate, high porosity, unmelted particles, undesirable oxides, or weak wear resistance and mechanical properties. The current research aimed to investigate the addition of ZrO2 as reinforcement to the self-fluxing alloy coatings. Mechanically mixed NiCrBSi-ZrO2 powders were thermally sprayed onto an industrially relevant high-grade steel. After thermal spraying, the samples were differently post-processed with a flame gun and with a vacuum furnace, respectively. Scanning electron microscopy showed a porosity reduction for the vacuum-heat-treated samples compared to that of the flame-post-processed ones. X-ray diffraction measurements showed differences in the main peaks of the patterns for the thermal processed samples compared to the as-sprayed ones, these having a direct influence on the mechanical behavior of the coatings. Although a slight microhardness decrease was observed in the case of vacuum-remelted samples, the overall low porosity and the phase differences helped the coating to perform better during wear-resistance testing, realized using a ball-on-disk arrangement, compared to the as-sprayed reference samples.
The printing variable least addressed in previous research aiming to reveal the effect of the FFF process parameters on the printed PLA part’s quality and properties is the filament color. Moreover, the color of the PLA, as well as its manufacturer, are rarely mentioned when the experimental conditions for the printing of the samples are described, although current existing data reveal that their influence on the final characteristics of the print should not be neglected. In order to point out the importance of this influential parameter, a natural and a black-colored PLA filament, produced by the same manufacturer, were selected. The dimensional accuracy, tensile strength, and friction properties of the samples were analyzed and compared for printing temperatures ranging from 200 C up to 240 C. The experimental results clearly showed different characteristics depending on the polymer color of samples printed under the same conditions. Therefore, the optimization of the FFF process parameters for the 3D-printing of PLA should always start with the proper selection of the type of the PLA material, regarding both its color and the fabricant.
Among the FDM process variables, one of the less addressed in previous research is the filament color. Moreover, if not explicitly targeted, the filament color is usually not even mentioned.
Aiming to point out if, and to what extent, the color of the PLA filaments influences the dimensional precision and the mechanical strength of FDM prints, the authors of the present research carried out experiments on tensile specimens. The variable parameters were the layer height (0.05 mm, 0.10 mm, 0.15 mm, 0.20 mm) and the material color (natural, black, red, grey). The experimental results clearly showed that the filament color is an influential factor for the dimensional accuracy as well as for the tensile strength of the FDM printed PLA parts. Moreover, the two way ANOVA test performed revealed that the strongest effect on the tensile strength was exerted by the PLA color (2 = 97.3%), followed by the layer height (2 = 85.5%) and the interaction between the PLA color and the layer height (2 = 80.0%). Under the same printing conditions, the best dimensional accuracy was ensured by the black PLA (0.17% width deviations, respectively 5.48% height deviations), whilst the grey PLA showed the highest ultimate tensile strength values (between 57.10 MPa and 59.82 MPa).
In this study, the characteristics of HVOF sprayed WC/Co-Cr and WC/Cr3C2/Ni coatings were investigated in correlation with the variation of the powder feed rate. For this purpose, the mass flow was adjusted to four different levels. The other process parameters were all kept constant. The morphological and mechanical properties as well as the electrochemical corrosion behaviour were investigated and associated with the achieved microstructure.
Both scanning electron microscopy and confocal laser scanning microscopical images of the cross sections demonstrated a good correlation between the selected powder feed rate and the degree of internal porosity produced, which can be attributed to the deposition process. The coatings which fulfilled the requirements of the pre-qualification step were selected for further hardness measurements, tribological tests and electrochemical corrosion measurements in a 3.5 wt% NaCl aqueous solution.
It was found that the powder feed rate strongly influenced the characteristics of the HVOF-sprayed cermet coatings. The tendency to crack formation, especially at the interface coating/substrate, was lower for the samples coated with a lower mass flow rate. These studies have shown that the applied powder feed rates had an important influence on the coatings microstructure and implicitly on the sliding wear behavior respectively on the electrochemical corrosion resistance of the investigated cermet coatings.
This paper aims to compare cobalt-based (type Stellite 6) and nickel-based self-fluxing alloys (type NiCrBSiMo) regarding both their cavitation erosion resistance and corrosion resistance. The two types of protective layers were thermally sprayed onto a substrate of martensitic stainless steel. In order to improve the layers' characteristics and their metallurgical bonding to the substrate, the Stellite 6 coating was laser remelted, while the NiCrBSiMo coating was treated by flame fusion. The cavitation erosion resistance of the two materials was evaluated by measurements of the mean depth of erosion developed during a testing period of 165 minutes, using a 20 kHz ultrasonic vibrator at a peak-to-peak amplitude of 50 μm. In addition, the corrosion resistance of the layers was assessed by potentiodynamic corrosion tests carried out in H2SO4 + NaCl solution at room temperature, using calomel as reference electrode. In order to highlight the differences regarding the behaviour of the two protective materials, the authors also carried out microstructural investigations of the layers before and after exposure to cavitation and corrosion. The investigations showed that both types of layers can provide improved protection of the martensitic stainless steel substrate against cavitation, whilst the NiCrBSiMo coating additionally confers significantly increased resistance to corrosion.
Optimization of the laser remelting process for HVOF-sprayed Stellite 6 wear resistant coatings
(2016)
Cobalt base alloys are used in all industrial areas due to their excellent wear resistance. Several studies have shown that Stellite 6 coatings are suitable not only for protection against sliding wear, but also in case of exposure to impact loading. In this respect, a possible application is the protection of hydropower plant components affected by cavitation. The main problem in connection with Stellite 6 is the deposition procedure of the protective layers, both welding and thermal spraying techniques requesting special measures in order to prevent the brittleness of the coating. In this study, Stellite 6 layers were HVOF thermally sprayed on a martensitic 13-4 stainless steel substrate, as usually used for hydraulic machinery components. In order to improve the microstructure of the HVOF-sprayed coatings and their adhesion to the substrate, laser remelting was applied, using a TRUMPF Laser type HL 124P LCU and different working parameters. The microstructure of the coatings, obtained for various remelting conditions, was evaluated by light microscopy, showing the optimal value of the pulse power, which provided a homogenous Stellite 6 layer with good adhesion to the substrate.
Flame-sprayed NiCrBSi/WC-12Co composite coatings were deposited in different ratios on the surface of stainless steel. Oxyacetylene flame remelting treatment was applied to surfaces for refinement of the morphology of the layers and improvement of the coating/substrate adhesion.
The performance of the coated specimens to cavitation erosion and electrochemical corrosion was evaluated by an ultrasonic vibratory method and, respectively, by polarization measurements. The microstructure was investigated by means of scanning electron microscopy (SEM) combined with energy dispersive X-ray analysis (EDX). The obtained results demonstrated that the addition of 15 wt.% WC-12Co to the self-fluxing alloy improves the resistance to cavitation erosion (the terminal erosion rate (Vs) decreased with 15% related to that of the NiCrBSi coating) without influencing the good corrosion resistance in NaCl solution. However, a further increase in WC-Co content led to a deterioration of these coating properties (the Vs has doubled related to that of the NiCrBSi coating).
Moreover, the corrosion behavior of the latter composite coating was negatively influenced, a fact confirmed by increased values for the corrosion current density (icorr). Based on the achieved experimental results, one may summarize that NiCrBSi/WC-Co composite coatings are able to increase the life cycle of expensive, high-performance components exposed to severe cavitation conditions.