For proton exchange membrane water electrolysis (PEMWE) to become competitive, the cost of stack components, such as bipolar plates (BPP), needs to be reduced. This can be achieved by using coated low-cost materials, such as copper as alternative to titanium. Herein we report on highly corrosion-resistant copper BPP coated with niobium. All investigated samples showed excellent corrosion resistance properties, with corrosion currents lower than 0.1 µA cm−2 in a simulated PEM electrolyzer environment at two different pH values. The physico-chemical properties of the Nb coatings are thoroughly characterized by scanning electron microscopy (SEM), electrochemical impedance spectroscopy (EIS), X-ray photoelectron spectroscopy (XPS), and atomic force microscopy (AFM). A 30 µm thick Nb coating fully protects the Cu against corrosion due to the formation of a passive oxide layer on its surface, predominantly composed of Nb2O5. The thickness of the passive oxide layer determined by both EIS and XPS is in the range of 10 nm. The results reported here demonstrate the effectiveness of Nb for protecting Cu against corrosion, opening the possibility to use it for the manufacturing of BPP for PEMWE. The latter was confirmed by its successful implementation in a single cell PEMWE based on hydraulic compression technology.
The present paper presents one- and two-step approaches for electrochemical Pt and Ir deposition on a porous Ti-substrate to obtain a bifunctional oxygen electrode. Surface pre-treatment of the fiber-based Ti-substrate with oxalic acid provides an alternative to plasma treatment for partially stripping TiO2 from the electrode surface and roughening the topography. Electrochemical catalyst deposition performed directly onto the pretreated Ti-substrates bypasses unnecessary preparation and processing of catalyst support structures. A single Pt constant potential deposition (CPD), directly followed by pulsed electrodeposition (PED), created nanosized noble agglomerates. Subsequently, Ir was deposited via PED onto the Pt sub-structure to obtain a successively deposited PtIr catalyst layer. For the co-deposition of PtIr, a binary PtIr-alloy electrolyte was used applying PED. Micrographically, areal micro- and nano-scaled Pt sub-structure were observed, supplemented by homogenously distributed, nanosized Ir agglomerates for the successive PtIr deposition. In contrast, the PtIr co-deposition led to spherical, nanosized PtIr agglomerates. The electrochemical ORR and OER activity showed increased hydrogen desorption peaks for the Pt-deposited substrate, as well as broadening and flattening of the hydrogen desorption peaks for PtIr deposited substrates. The anodic kinetic parameters for the prepared electrodes were found to be higher than those of a polished Ir-disc.
Various aqueous citrate electrolyte compositions for the Ni-Mo electrodeposition are explored in order to deposit Ni-Mo alloys with Mo-content ranging from 40 wt% to 65 wt% to find an alloy composition with superior catalytic activity towards the hydrogen evolution reaction (HER). The depositions were performed on copper substrates mounted onto a rotating disc electrode (RDE) and were investigated via scanning electron microscopy (SEM), X-ray fluorescence (XRF) and X-ray diffraction (XRD) methods as well as linear sweep voltammetry (LSV) and impedance spectroscopy. Kinetic parameters were calculated via Tafel analysis. Partial deposition current densities and current efficiencies were determined by correlating XRF measurements with gravimetric results. The variation of the electrolyte composition and deposition parameters enabled the deposition of alloys with Mo-content over the range of 40-65 wt%. An increase in Mo-content in deposited alloys was recorded with an increase in rotation speed of the RDE. Current efficiency of the deposition was in the magnitude of <1%, which is characteristic for the deposition of alloys with high Mo-content. The calculated kinetic parameters were used to determine the Mo-content with the highest catalytic activity for use in the HER.
In this work, a novel polymer electrolyte membrane water electrolyzer (PEMWE) test cell based on hydraulic single-cell compression is described. In this test cell, the current density distribution is almost homogeneous over the active cell area due to hydraulic cell clamping. As the hydraulic medium entirely surrounds the active cell components, it is also used to control cell temperature resulting in even temperature distribution. The PEMWE single-cell test system based on hydraulic compression offers a 25 cm2 active surface area (5.0 × 5.0 cm) and can be operated up to 80°C and 6.0 A/cm2. Construction details and material selection for the designed test cell are given in this document. Furthermore, findings related to pressure distribution analyzed by utilizing a pressure-sensitive foil, the cell performance indicated by polarization curves, and the reproducibility of results are described. Experimental data indicate the applicability of the presented testing device for relevant PEMWE component testing and material analysis.
Hydrogen produced via water electrolysis powered by renewable electricity or green H2 offers new decarbonization pathways. Proton exchange membrane water electrolysis (PEMWE) is a promising technology although the current density, temperature, and H2 pressure of the PEMWE will have to be increased substantially to curtail the cost of green H2. Here, a porous transport layer for PEMWE is reported, that enables operation at up to 6 A cm−2, 90 °C, and 90 bar H2 output pressure. It consists of a Ti porous sintered layer (PSL) on a low‐cost Ti mesh (PSL/mesh‐PTL) by diffusion bonding. This novel approach does not require a flow field in the bipolar plate. When using the mesh‐PTL without PSL, the cell potential increases significantly due to mass transport losses reaching ca. 2.5 V at 2 A cm−2 and 90 °C.
A systematic method for obtaining a novel electrode structure based on PtCoMn ternary alloy catalyst supported on graphitic carbon nanofibers (CNF) for hydrogen evolution reaction (HER) in acidic media is proposed. Ternary alloy nanoparticles (Co0.6Mn0.4 Pt), with a mean crystallite diameter under 10 nm, were electrodeposited onto a graphitic support material using a two-step pulsed deposition technique. Initially, a surface functionalisation of the carbon nanofibers is performed with the aid of oxygen plasma. Subsequently, a short galvanostatic pulse electrodeposition technique is applied. It has been demonstrated that, if pulsing current is employed, compositionally controlled PtCoMn catalysts can be achieved. Variations of metal concentration ratios in the electrolyte and main deposition parameters, such as current density and pulse shape, led to electrodes with relevant catalytic activity towards HER. The samples were further characterised using several physico-chemical methods to reveal their morphology, structure, chemical and electrochemical properties. X-ray diffraction confirms the PtCoMn alloy formation on the graphitic support and energy dispersive X-ray spectroscopy highlights the presence of the three metallic components from the alloy structure. The preliminary tests regarding the electrocatalytic activity of the developed electrodes display promising results compared to commercial Pt/C catalysts. The PtCoMn/CNF electrode exhibits a decrease in hydrogen evolution overpotential of about 250 mV at 40 mA cm−2 in acidic solution (0.5 M H2SO4) when compared to similar platinum based electrodes (Pt/CNF) and a Tafel slope of around 120 mV dec−1, indicating that HER takes place under the Volmer-Heyrovsky mechanism.